hdi diourea asahikasei  22a-75px

 

type :

aliphatic polyisocyanate (hdi biuret）

features:

# good coated film appearance

# good adhesion

# good weather resistance

applications:

# two-component applications

# plastic coatings

# auto refinish coatings

# automobile, motorcycle; base coat and top coat# heavy duty coatings

typical properties：

appearance	colorless to slightly yellowish clear liquid
non-volatile	75 wt%
solvent	methoxypropylacetate (pma)xylene=1/1
nco content	16.5 wt%
viscosity	210mpa .s at 25°c
color value	<1 (gardner)
nco equivalent weight	approx.254
flash point	39°c
density at 20°c	1.07

these values provide general information and are not part of the product specifications.

stability / thinnability:

duranatetm 22a-75px can be thinned with esters, ketones and aromatic.hydrocarbons such as ethyl acetate, butyl acetate, methoxypropylacetate (pma),methyl ethyl ketone, methyl-butyl ketone, cyclohexanone, toluene, xylene, solvesso#100 and mixture thereof. generally speaking, it has good compatibility with thesolvents mentioned. however, the solutions formed must be tested for their storagestability.

only pu grade solvents can be used (max. 0.05% water, absence of reactive groupssuch as hydroxyl or amines groups). aliphatic hydrocarbons such as hexane,cyclohexane, methylcyclohexanes and mineral spirits, are unsuitable as solventsbecause of their poor solubility.

duranatetm 22a-75px should not be thinned to below a solid content of 40%.prolonged storage of solution with lower solid content may result in turbidity andsedimentation.

compatibility:

 

 

mixing ratio of duranatetm 22a-75px with polyols is based on nco/oh equivalentratio of 1/1 .

storage:

duranatetm 22a-75px is sensitive to moisture and should therefore always bestored in sealed containers.

 

characteristics of viscosity

 

 

weatherability

 